1、ck 内凹或吸入is condition where the weld metal has contracted as it cools and has been drawn up into the root of the weld. On a radiograph it looks similar to lack of penetration but the line has irregular edges and it is often quite wide in the center of the weld image.Internal or root undercut 内部或根部咬边i
2、s an erosion of the base metal next to the root of the weld. In the radiographic image it appears as a dark irregular line offset from the centerline of the weldment. Undercutting is not as straight edged as LOP because it does not follow a ground edge.External or crown undercut 外部或顶部咬边is an erosion
3、 of the base metal next to the crown of the weld. In the radiograph, it appears as a dark irregular line along the outside edge of the weld area. Offset or mismatch 错边are terms associated with a condition where two pieces being welded together are not properly aligned. The radiographic image is a no
4、ticeable difference in density between the two pieces. The difference in density is caused by the difference in material thickness. The dark, straight line is caused by failure of the weld metal to fuse with the land area.Inadequate weld reinforcement 未填满is an area of a weld where the thickness of w
5、eld metal deposited is less than the thickness of the base material. It is very easy to determine by radiograph if the weld has inadequate reinforcement, because the image density in the area of suspected inadequacy will be more (darker) than the image density of the surrounding base material.Excess
6、 weld reinforcement 增强余高is an area of a weld, which has weld metal added in excess of that specified by engineering drawings and codes. The appearance on a radiograph is a localized, lighter area in the weld. A visual inspection will easily determine if the weld reinforcement is in excess of that sp
7、ecified by the individual code involved in the inspection.Cracking 裂纹can be detected in a radiograph only the crack is propagating in a direction that produced a change in thickness that is parallel to the x-ray beam. Cracks will appearas jagged and often very faint irregular lines. Cracks can somet
8、imes appearing as tails on inclusions or porosity.Discontinuities in TIG weldsThe following discontinuities are peculiar to the TIG welding process. These discontinuities occur in most metals welded by the process including aluminum and stainless steels. The TIG method of welding produces a clean ho
9、mogeneous weld which when radiographed is easily interpreted.Tungsten inclusions. 夹钨Tungsten is a brittle and inherently dense material used in the electrode in tungsten inert gas welding. If improper welding procedures are used, tungsten may be entrapped in the weld. Radiographically, tungsten is m
10、ore dense than aluminum or steel; therefore, it shows as a lighter area with a distinct outline on the radiograph.Oxide inclusions 夹氧化物are usually visible on the surface of material being welded (especially aluminum). Oxide inclusions are less dense than the surrounding materials and, therefore, app
11、ear as dark irregularly shaped discontinuities in the radiograph.Discontinuities in Gas Metal Arc Welds (GMAW)The following discontinuities are most commonly found in GMAW welds.Whiskers are short lengths of weld electrode wire, visible on the top or bottom surface of the weld or contained within th
12、e weld. On a radiograph they appear as light, wire like indications.Burn through (icicles) results when too much heat causes excessive weld metal to penetrate the weld zone. Lumps of metal sag through the weld creating a thick globular condition on the back of the weld. On a radiograph, burn through
13、 appears as dark spots surrounded by light globular areas.welld-02 (Incomplete Root Fusion、根部未熔合)welld-03 (Insuffucient Reinforcement、增强高)welld-04 (Excess Root Penetration、根部焊瘤)welld-05 (External Undercut、外部咬肉)welld-06 (Internal Undercut、内部咬肉)welld-07 (Root Concavity、根部凹陷)welld-08 (Burn Through、烧穿)最
14、瀀栀琀洀氀趹/Ia前台访问/p-27994.html207.46.13.410%挀搀栀琀洀氀頀趻/Mi前台访问/p-3472678.html116.179.32.2430%掠最搀栀琀洀氀趼5gwap前台访问/BookRead.aspx?id=3169174111.206.198.750匀焀眀愀瀀瀀栀琀洀氀趼/Mg前台访问/p-1382269.html157.55.39.1520%掠攀瀀栀琀洀氀趽/So前台访问/order-326285.html114.239.58.1520%匀焀眀愀瀀搀栀琀洀氀趽/Mk前台访问/p-3263993.html220.181.108.1170聠最蔀眀愀瀀漀漀欀刀攀愀搀愀猀瀀砀椀搀趿/Me前台访问/p-2673368.html207.46.13.410勈証劰椀搀栀琀洀氀跀/Ma前台访问/p-3464229.html49.74.2.130攀瀀栀琀洀氀琀跁/Me前台访问/p-2114122.html157.55.39.680%椀瀀栀琀洀氀跂5Sowap前台访问/d-1932916.html116.179.32.1630勈証匀洀眀愀瀀瀀栀琀洀氀跃/Mi前台访问/p-3284350.html220.181.108.920%掠攀瀀栀琀洀氀跃/Me前台访问/d-1360381.html157.55.39.680%棹